Corrosion Resistance of Aluminized Diffusion coating for Fe-25Cr-20Ni steel
Min Jung Kim, Dong Bok Lee
School of Advanced Materials Science & Engineering, Sungkyunkwan University, Suwon 16419, Korea.
Abstract: High-temperature corrosion resistance and characteristics of Fe-25Cr-20Ni steel was studied at 800 oC in air and (N2/H2O/H2S)-mixed gas condition up to 100 hours. The weight gain of each test coupon after the oxidation and (N2/H2O/H2S)-mixed gas corrosion test was measured using a micro-balance. The corroded test coupons were characterized by a SEM, an EDS, an XRD with Cu-Kα radiation, and an EPMA. As a result of the experiments, aluminized diffusion coating was formed the FeAl2 intermetallic phases. Thus aluminized diffusion coated Fe-25Cr-20Ni steel has reasonable corrosion resistance, because it can form a protective alumina scale, such as α-Al2O3 layer.
Key words: Corrosion, aluminized diffusion coating, Fe-25Cr-20Ni steel, oxidation, sulfidation.
Cite: Min Jung Kim, Dong Bok Lee, "Corrosion Resistance of Aluminized Diffusion coating for Fe-25Cr-20Ni steel," International Journal of Materials Science and Engineering, Vol. 8, No. 1, pp. 93-98, March 2020. doi: 10.17706/ijmse.2020.8.1.15-19
Key words: Corrosion, aluminized diffusion coating, Fe-25Cr-20Ni steel, oxidation, sulfidation.
Cite: Min Jung Kim, Dong Bok Lee, "Corrosion Resistance of Aluminized Diffusion coating for Fe-25Cr-20Ni steel," International Journal of Materials Science and Engineering, Vol. 8, No. 1, pp. 93-98, March 2020. doi: 10.17706/ijmse.2020.8.1.15-19
General Information
ISSN: 2315-4527 (Print)
Abbreviated Title: Int. J. Mater. Sci. Eng.
Editor-in-Chief: Prof. Emeritus Dato' Dr. Muhammad Yahaya
DOI: 10.17706/ijmse
Abstracting/ Indexing: Ulrich's Periodicals Directory, Google Scholar, Crossref
E-mail: ijmse@iap.org
What's New
-
Oct 29, 2022 News!
-
May 26, 2022 News!
The dois of the papers published in Volume 10, Number 2 have all been activated by Crossref.
-
May 26, 2022 News!
-
Feb 17, 2022 News!
-
Nov 08, 2021 News!
- Read more>>