Fractional Recrystallization Behaviour of Al-Mg Alloy with Different Sc Addition Content
M. S. Kaiser
Directorate of Advisory, Extension and Research Services, Bangladesh University of Engineering and Technology, Dhaka-1000, Bangladesh
Abstract—Recrystallization kinetics of 75% cold rolled Al-6Mg alloy with ternary scandium is analyzed from the micro-hardness variation. Isothermally annealed aluminum alloy samples were also studied using JMAK type analysis to see if there exists any correlation between the methods. Recrystallization fraction between two methods, the scandium added alloys show the higher variation due to precipitation hardening and higher recrystallization behavior. From the microstructure it is also observed that the base Al-Mg alloy attained almost fully re-crystallized state after annealing at 400°C for 60 minutes.
Index Terms—Al-Mg alloys, annealing, hardness, recrystallization, precipitate
Cite: M. S. Kaiser, "Fractional Recrystallization Behaviour of Al-Mg Alloy with Different Sc Addition Content," International Journal of Materials Science and Engineering, Vol. 2, No. 2, pp. 136-140, December 2014. doi: 10.12720/ijmse.2.2.136-140
Cite: M. S. Kaiser, "Fractional Recrystallization Behaviour of Al-Mg Alloy with Different Sc Addition Content," International Journal of Materials Science and Engineering, Vol. 2, No. 2, pp. 136-140, December 2014. doi: 10.12720/ijmse.2.2.136-140
General Information
ISSN: 2315-4527 (Print)
Abbreviated Title: Int. J. Mater. Sci. Eng.
Editor-in-Chief: Prof. Emeritus Dato' Dr. Muhammad Yahaya
DOI: 10.17706/ijmse
Abstracting/ Indexing: Ulrich's Periodicals Directory, Google Scholar, Crossref
E-mail: ijmse@iap.org
What's New
-
Oct 29, 2022 News!
-
May 26, 2022 News!
The dois of the papers published in Volume 10, Number 2 have all been activated by Crossref.
-
May 26, 2022 News!
-
Feb 17, 2022 News!
-
Nov 08, 2021 News!
- Read more>>